MJF PA11 — Ductile HP Nylon
Bio-sourced HP MJF material for impact-critical production parts.
MJF PA11 brings the ductility and impact resistance of PA11 into the high-throughput HP Multi Jet Fusion process. It provides higher elongation at break and improved toughness vs MJF PA12CB while retaining the near-isotropic consistency of the MJF process. Particularly suited for functional parts that must survive mechanical shock without brittle fracture.
Starting from €30 / part · Lead time from 2 business days
Key Technical Values
Tensile Strength
Stiffness (E)
Heat Defl. Temp
Under load
Elongation
Density
Hardness
ℹ ASTM D638 / ASTM D256 / ASTM D648.
Mechanical Properties
| Property | Value | Unit |
|---|---|---|
| Tensile Strength | 52 | MPa |
| Tensile Modulus (E) | 1700 | MPa |
| Elongation at Break | 25 | % |
| Notched Impact Strength | 6 | kJ/m² |
| Heat Deflection Temp (HDT) | 145 | °C |
| Density | 1.01 | g/cm³ |
| Hardness | 73 Shore D |
Recommended Applications
Impact-resistant production parts
Snap-fits with large flexure travel
Wearable and consumer product components
Medical device housings (check certification)
Not Recommended For
Maximum stiffness requirements
Parts above 150 °C continuous service
Order & Documentation
Available Finishes / Colours
Compare Materials
Related Materials
MJF Technology
HP Multi Jet Fusion fuses PA powder using a thermal print head and absorber agents — enabling batch consistency across large production volumes.
Learn about MJFReady to order MJF PA11 parts?
Upload your CAD file for an instant quote, or contact our team for material selection advice.